![]() ![]() ![]() ![]() Stannol Contact Soldering Paste is not suitable for fresh water and tap water pipes. Flux residues must be removed for applications in the electronics field. Appropriate soldering tins are leaded solders such as Sn60Pb40, Pb70Sn30 and leadfree solders such as Sn99Cu1, Sn96Ag4. The temperature of the solder joints should be at least 50 degrees above the melting point (melting range) of the solder. Soft solder paste for reliable connections of potable water and gas boiler pipework installations. The use of petrolatum is disadvantageous. LA-CO Regular Soldering Flux Paste 60g (22103). soldering iron) and supply soldering tin. Most soldering paste fluxes currently in use are petrolatum-based and usually contain zinc and ammonium chloride. Heat the solder joint with a suitable device (e.g. ![]() Apply Stannol Contact Soldering Paste on the metal to be soldered. The solder joints should be clean and free from surface layers, grind if necessary. Removing flux residues is not necessary as these are not corrosive. Some application examples are: cable tinning, soldering of connections and shields and repair of leads. Stannol Contact Soldering Paste is a flux for general soldering and is preferably used for soldering of copper and copper alloys, nickel and nickel alloys and is suitable for applications in electrical engineering. La-Co Regular Soldering Flux PasteWater-soluble paste wont leave residue in water piping.Meets industry standard ASTM B813 and contains no zinc chloride. LA-CO Regular Flux is the ultimate flux for all copper soldering applications, the all-weather water-soluble paste wont leave residue in water piping and. This solder resin cleans and prevents metal oxidation. 144 are water-soluble.The Stannol Contact Soldering Paste is a preparation of activated colophonium resin in mineral fats. Solder Flux Rosin Paste 15g Rosin flux is used to facilitate soldering. 144 is also an excellent choice for badly oxidized copper. 144 can be precision dispensed either automatically or manually, or applied with a brush or similar implement. This soldering flux was specifically formulated for situations where dispensing is required for a stainless steel soldering application. The flux is active and contains zinc chloride and is suitable for soldering many metals including copper, brass and mild steel. 144 is a unique Water-Soluble paste flux. 79 is an Acid-Free flux formulated for stainless steel, high-chrome alloys and other general soldering applications. Due to its high viscosity, the gel flux does not migrate upon heating, providing a more restrictive solder flow. Solder flux contributes to achieving a perfect soldering bond, which is activated by the heat of the soldering operation to remove the. 78 is a gel form stainless steel soldering flux. 75 is a inorganic acid, general purpose flux for stainless steel. Flux paste offers good soldering performance for rugged and stable application. Fluoride etches glass, and thus this flux should not be used on parts where glass etching would be an issue. 71 contains Zinc Chloride, Ammonium Chloride, Hydrochloric Acid and a fluoride activator. 71 is our most active flux for soldering stainless steel. LA-CO Regular Flux is the ultimate flux for all copper soldering applications, the all-weather water-soluble paste won’t leave residue in water piping and contains no zinc chloride to reduce corrosion concerns. 71 is a high-activity Zinc Chloride flux formulated for situations where a general-purpose soft soldering flux is not strong enough for badly oxidized or difficult-to-solder metals like stainless steels, Monel, High-Chrome alloys and Inconel. ![]()
0 Comments
Leave a Reply. |
AuthorWrite something about yourself. No need to be fancy, just an overview. ArchivesCategories |